Introduction to Pressure Casting

Pressure casting is a casting method in which molten or semi-molten metal is pressed into the metal vowin.cn/' target='_blank'>casting vowin.cn/' target='_blank'>mold
at high speed and crystallized under pressure, referred to as die casting. 

Advantages Of Pressure Casting

1) High productivity, easy-to-achieve mechanization, and automation, can produce thin-walled castings with
complex shapes. The minimum wall thickness of die-casting zinc alloy is only 0.3mm, the minimum wall thickness
of die-casting aluminum alloy is about 0.5mm, and the minimum cast out hole diameter is 0.7mm.

2) High dimensional accuracy of castings, small surface roughness value. Die casting size tolerance grade up to
CT3 ~ CT6, the surface roughness is generally Ra0.8 ~ 3.2μm. 

3) Pressure casting parts can be embedded in the casting parts, not only to save valuable materials and machining
hours, but also to replace the assembly process of the parts, can eliminate the assembly process, simplify the
manufacturing process. 

Application Of Pressure Casting 

Due to the advantages of pressure casting, it is widely used, mainly in mass production of non-ferrous alloy castings. 
Pressure die casting applications are the most automobile, tractor manufacturing, followed by instrument manufacturing
and electronic instrument industry, again for agricultural machinery, defense industry, computers, medical equipment and
other manufacturing industries. The parts produced by die-casting method are engine cylinder block, cylinder head,
transmission case, engine cover, instrumentation and camera shell and bracket, pipe fittings, gears, etc.. In recent years,
high technology has been applied to the field of pressure casting. Such as the use of three-stage pressure injection
mechanism to control the pressure, injection speed and gas in the mold. Development of special pressure casting process
(such as vacuum die-casting, directional pressure casting, oxygen die-casting, etc.) and the application of computer control
technology to effectively remove the pores, improve the density of the casting, while developing new mold materials and heat
treatment of new technology to extend the life of the die, so that ferrous metal die-casting has made some progress.